Ropes & accessories Work at height

ANTIPODES ANTIPODES 9 mm Semi-static type B rope, ultra light but requiring greater attention during use. ANTIPODES 10 mm The lightest of the ropes having a margin of security suffi cient for use for work ANTIPODES 10,5 m Extra mass and strength - the standard for work at height. ANTIPODES 11 et 11,5 mm Great reserves of strength and abrasion resistance for the hardest application 11 mm INDUSTRIE This rope is specially adapted to the needs of the constuction industry. HD ROPES

DUREE 20 mn 10,5 mm TOP WORK Rope particularly resistant to wear due to a much increased percentage of sheath. 11 mm NORTH SEA Specially developed in conjunction with a major oil producing company for use on oil rigs in hostile conditions. 10,5 mm CONTRACT Type A ropes with the best balance of quality/price.

Semi-static rope which allows access to areas with raised temperatures or in the presence of certain chemical products. The aramide part of the rope’s sheath can withstand limited exposure at up to 300°C. Its strength of 820kg may give residual security should the polyamide content melt. Its strength deteriorates rapidly above 500°C.. RELATIONSHIP BETWEEN THE TIME OF EXPOSURE TO HIGH TEMPERATURE AND THE RESIDUAL STRENGTH OF THE ARAMIDE CHEMICAL RESISTANCE OF ARAMIDE FILAMENT (ambient conditions) Exposure for 100h at 21°C Tenacity loss in % ACIDS formic 90% 10% hydochloric 37% 90% hydrofluoric 10% 12% nitric 70% 82% sulphuric 70% 100% BASES ammonia - 24 h 0% Potassium - 24 h 25% Sodium - 24 h 10% OTHER CHIMICAL PRODUCTS brake fluid 312 h 2% Grease (base MoS and Lithium) 0% Kerosene (JP-4) 300 h 0% Ozone - 1000 h 0% Tap water 0% Boiling water 0% Superheated water 156°C - 80 h 16%

ANTIPODES
	9 mm	10 mm	10,5 mm
Type of rope Diameter Breaking load Strength with figure 8 knot Strength with figure 9 knot Strength with sewn terminations Number of factor 1 falls Impact Force - Factor 0,3 Elongation 50/150KG Sheath slippage Weight per metter Sheath percentage Core percentage Shrinkage in water Material	B 9 mm 1900 daN (kg) 1350 daN (kg) 1600 daN (kg) - 8 (80 kg) 4.00 kN 3,6 % 0,3 % 51 g 43 % 57 % 4 % Polyamid (PA)	A 10 mm 2400 daN (kg) 1700 daN (kg) 1800 daN (kg) 2000 daN (Kg) 6 (100 kg) 4.30 kN 4,4 % 0 % 62 g 43 % 57 % 4 % Polyamid (PA)	A 10,5 mm 2700 daN (kg) 1950 daN (kg) 2100 daN (kg) 2400 daN (kg) 16 (100 kg) 5.10 kN 3,0 % 0,8 % 65 g 38 % 62 % 5 % Polyamid (PA)

ANTIPODES
	11 mm	11,5 mm
Type of rope Diameter Breaking load Strength with figure 8 knot Strength with figure 9 knot Strength with sewn terminations Number of factor 1 falls Impact Force - Factor 0,3 Elongation 50/150KG Sheath slippage Weight per metter Sheath percentage Core percentage Shrinkage in water Material	A 11 mm 3000 daN (kg) 2100 daN (kg) 2200 daN (kg) 2400 daN (kg) 20 (100 kg) 5.10 kN 2,8 % 0,8 % 73 g 36 % 64 % 4 % Polyamid (PA)	A 11,5 mm 3200 daN (kg) 2300 daN (kg) 2400 daN (kg) 2600 daN (kg) > 20 (100 kg) 5.30 kN 2,6 % 0,5 % 78 g 38 % 62 % 5 % Polyamid (PA)

PERFORMANCE	Indusrie 11 mm	Top work 10,5 mm	North Sea 11 mm	Contract 10,5 mm
Type of rope Diameter Breaking load Strength with figure 8 knot Strength with figure 9 knot Strength with sewn terminations Number of factor 1 falls Impact Force - Factor 0,3 Elongation 50/150KG Sheath slippage Weight per metter Sheath percentage Core percentage Shrinkage in water Material	A 11 mm 3000 daN (kg) 2100 daN (kg) 2200 daN (kg) 2200 daN (kg) 20 (100 kg) 5.10 kN 2,8 % 0,8 % 73 g 36 % 64 % 4 % Polyamid (PA)	A 10,5 mm 2600 daN (kg) 1900 daN (kg) 2000 daN (kg) - 15 (100 kg) 4.60 kN 4,8 % 0,3 % 64 g 44 % 56 % 3,5 % Polyamid (PA)	A 11 mm 3000 daN (kg) 1900 daN (kg) 2000 daN (kg) - > 20 (100 kg) 5.10 kN 4,0 % 0,9 % 75 g 44 % 56 % 3 % Polyamid (PA)	A 10,5 mm 2500 daN (kg) 1750 daN (kg) 2000 daN (kg) - 12 (100 kg) 5.60 kN 3,0 % 0 mm 68 g 36 % 64 % 4 % Polyamid (PA)

PERFORMANCE	Hotline 11 mm
Type of rope Diameter Breaking load Strength with figure 8 knot Number of factor 1 falls Impact Force - Factor 0,3 Elongation 50/150KG Sheath slippage Weight per metter Sheath percentage Core percentage Shrinkage in water Sheath material Material core Temperature maximum for extended use T° at which the aramide decomposes Melting point of the polyamide core Strength of aramide core sheath	A 11 mm 2500 daN (kg) 1900 daN (kg) 15 (100 kg) 5.60 kN 3,1 % 0 % 79 g 42 % 58 % 3,3 % Polyamid (PA) Polyamid (PA) /Aramid (PPTA) 180 °C 500 °C 230 °C 820 kg

Protector A rope may wear extremely rapidly over an abrasive edge. To protect it, use the Protector, an ultra tough rope protector made with two layers of coated material. - Length: 70 cm - Weight: 150 g HD Protector Video Work at height. Training video to learn how to deploy your rope at the worksite, how to look after it, and to control its use. Length: 20 mn VHS PAL/SECAM/NTSC	Transport bag “Combi pro” Equipped with a double opening and made from coated ripstop material, perfectly designed for carrying personal gear. - Volume: 30 l - Dimensions: 70x25 cm - Weight: 750 g HD Combi